Germanium Nitride Layers on Semiconductor Structures, and Methods for Forming the Same

ABSTRACT

Provided herein are semiconductor structures that include germanium and have a germanium nitride layer on the surface, as well as methods of forming the same. The described structures include nanowires and fins. Methods of the disclosure include metal-organic chemical vapor deposition with a germanium precursor. The described methods also include using a N 2 H 4  vapor.

PRIORITY CLAIM

This application is a divisional of U.S. application Ser. No.15/998,683, filed on Aug. 15, 2018, which application is herebyincorporated herein by reference.

BACKGROUND

Semiconductor nanowires and fins, such as those including germanium, areused in a variety of device applications (e.g., in field effecttransistors), and may include a surface passivation layer, which can beproduced using several techniques. Previously used surface passivationlayers are generally very thin (e.g., monolayer thickness) and mayinclude materials that alter the electrical characteristics of theresulting device, for example, materials that have a lattice mismatchwith the underlying semiconductor nanowire or fin, or materials thatform a dipole at the interface between the passivation layer and theunderlying semiconductor nanowire or fin.

BRIEF DESCRIPTION OF THE SEVERAL VIEWS OF THE DRAWINGS

Aspects of the present disclosure are best understood from the followingdetailed description when read with the accompanying figures. It isnoted that, in accordance with the standard practice in the industry,various features are not drawn to scale. In fact, the dimensions of thevarious features may be arbitrarily increased or reduced for clarity ofdiscussion.

FIGS. 1A-1E illustrate a method for forming a germanium nitride layer ona semiconductor structure, in accordance with some embodiments.

FIGS. 2A-2G illustrate a method for forming a germanium nitride layer ona semiconductor structure, in accordance with some embodiments.

FIG. 3 illustrates an example fabrication process.

DETAILED DESCRIPTION

The following disclosure provides many different embodiments, orexamples, for implementing different features of the provided subjectmatter. Specific examples of components and arrangements are describedbelow to simplify the present disclosure. These are, of course, merelyexamples and are not intended to be limiting. For example, the formationof a first feature over or on a second feature in the description thatfollows may include embodiments in which the first and second featuresare formed in direct contact, and may also include embodiments in whichadditional features may be formed between the first and second features,such that the first and second features may not be in direct contact. Inaddition, the present disclosure may repeat reference numerals and/orletters in the various examples. This repetition is for the purpose ofsimplicity and clarity and does not in itself dictate a relationshipbetween the various embodiments and/or configurations discussed.

Further, spatially relative terms, such as “beneath,” “below,” “lower,”“above,” “upper” and the like, may be used herein for ease ofdescription to describe one element or feature's relationship to anotherelement(s) or feature(s) as illustrated in the figures. The spatiallyrelative terms are intended to encompass different orientations of thedevice in use or operation in addition to the orientation depicted inthe figures. The apparatus may be otherwise oriented (rotated 90 degreesor at other orientations) and the spatially relative descriptors usedherein may likewise be interpreted accordingly.

Embodiments described herein include a germanium nitride (Ge₃N₄) layeron the surface of a semiconductor structure, e.g., a nanowire or fin,which comprises germanium (Ge). Such layers are more than a surfacetreatment, meaning that the germanium nitride layer is more than amonolayer thick. In embodiments, a germanium nitride layer is at leastabout 0.2 nanometers (nm) thick. “About,” as used herein, denotes thatthe actual value may be somewhat more or somewhat less than the statedvalue or range, to within ±20% of the stated value. In embodiments,about means that the actual value is within ±15% of the stated value. Insome embodiments, about means that the actual value is within ±10% ofthe stated value. In some embodiments, about means that the actual valueis within ±5% of the stated value. In some embodiments, about means thatthe actual value is within ±1% of the stated value.

In various embodiments, a germanium nitride layer of this disclosure hasa low carbon concentration, a low oxygen concentration, or both.Further, in some embodiments, an interface between a surface of asemiconductor structure and a germanium nitride layer has a lowinterface trap density (D_(IT)).

As described in more detail below, embodiments of the present disclosureinclude forming a semiconductor structure that comprises germanium, andforming a germanium nitride layer, which is more than a monolayer thick,on a surface of the semiconductor structure. In embodiments, thegermanium nitride layer is formed using metal-organic chemical vapordeposition (MOCVD). In some embodiments, the vapor used in the MOCVDcomprises Ge₂H₆, N₂H₄, or both.

Embodiments of the present disclosure include forming a germaniumnitride layer on a semiconductor structure under conditions that avoidreflow of germanium in the semiconductor structure. Additionally, insome embodiments, methods of forming a germanium nitride layer describedherein have substantially no inhibition time.

FIGS. 1A-1E illustrate steps of a method of the disclosure, inaccordance with some embodiments of the present disclosure. FIG. 3provides a flow chart that illustrates the steps of an illustrativemethod, in accordance with various embodiments of the presentdisclosure.

As shown in FIG. 1A, and as described in example operation 100 of FIG.3, a semiconductor structure 10 (e.g., a nanowire or a fin) is formed.In embodiments, semiconductor structure 10 includes germanium. In someembodiments, semiconductor structure 10 includes silicon and germanium.In some embodiments, semiconductor structure 10 includes two or moresections of different materials. For example, a semiconductor structuremay include a first section of germanium and a second section ofsilicon-germanium. In some embodiments, these different sections arestacked vertically (i.e., in a direction substantially perpendicular tothe surface of the substrate on which the semiconductor structure isarranged). In other embodiments, these different sections are arrangedhorizontally (i.e., in a direction substantially parallel to the surfaceof the substrate on which the semiconductor structure is arranged).

In accordance with various embodiments of the current disclosure,semiconductor structure 10 is formed using any suitable method. Suchmethods include lithographic techniques (e.g., photolithographic) andepitaxial growth.

In further embodiments, a dopant is implanted into semiconductorstructure 10, or a section thereof. In some embodiments, semiconductorstructure 10, or a section thereof, is doped with n-type dopant(s). Insome embodiments, semiconductor structure 10, or a section thereof, isdoped with p-type dopant(s). Any suitable process may be used to implantsuch a dopant into a semiconductor structure, or a section thereof.

In some embodiments, semiconductor structure 10 is formed on a substrate20. In some embodiments, semiconductor structure 10 is formed over asubstrate 20. In some embodiments, semiconductor structure 10 is incontact with a substrate 20. In some embodiments, semiconductorstructure 10 abuts a substrate 20. In other embodiments, semiconductorstructure 10 is formed from a substrate 20. For example, a semiconductorstructure 10 (e.g., a fin) may be formed by etching portions of asubstrate 20 on either side of a semiconductor structure 10.

Any suitable substrate may be used in the devices and methods of thisdisclosure. In embodiments, substrate 20 is a semiconductor material,e.g., silicon (Si), germanium, a silicon-germanium alloy, and the like.In some embodiments, the substrate 20 may comprise a compoundsemiconductor including Group Iv-Iv compound semiconductors such as SiCand SiGe, Group III-v compound semiconductors such as GaAs, GaP, GaN,InP, InAs, InSb, GaAsP, AlGaN, AlInAs, AlGaAs, GaInAs, GaInP, and/orGaInAsP; or combinations thereof. In embodiment, the substrate 20 is asilicon layer of an SOI (silicon-on insulator) substrate. Amorphoussubstrates, such as amorphous Si or amorphous SiC, or insulatingmaterial, such as silicon oxide may also be used as the substrate 20.The substrate 20 may include various regions that have been suitablydoped with impurities (e.g., p-type or n-type conductivity). Inembodiments, substrate 20 is a p-type silicon substrate with an impurityconcentration in a range of about 1×10¹⁵ cm⁻³ to about 2×10¹⁵ cm⁻³. Inother embodiments, the substrate 20 is an n-type silicon substrate withan impurity concentration in a range of about 1×10¹⁵ cm⁻³ to about2×10¹⁵ cm⁻³. In some embodiments, substrate 20 includes the samematerial as semiconductor structure 10.

In embodiments, a semiconductor structure 10 is a fin, as shown in FIG.1A. In other embodiments, a semiconductor structure 10 is a nanowire.

In some embodiments, a semiconductor structure 10 is a verticalsemiconductor structure, i.e., a semiconductor structure that extendsaway from a surface 25 of the substrate by a height 30 that is greaterthan the width 35 of the semiconductor structure. In some embodiments, avertical semiconductor structure is a vertical nanowire. In otherembodiments, a vertical semiconductor structure is a fin.

As shown in FIG. 1B, an isolating, insulating layer 50 is formed overthe semiconductor structure 10. In embodiments, insulating layer 50includes one or more layers of insulating materials such as siliconoxide, silicon oxynitride, or silicon nitride. The insulating layer 50can be formed by any suitable methods, for example, low pressurechemical vapor deposition (LPCVD), plasma CVD, and the like.

After forming the insulating layer 50, a planarization operation isperformed so as to remove part of the insulating layer 50. Theplanarization operation may include a chemical mechanical polishing(CMP), an etch-back process, or both.

Then, the insulating layer 50 is partially removed so that the channelregion in the semiconductor structure 10 is exposed. In embodiments, thepartial removal of the insulating layer 50 may be performed using a wetetching process, for example, by dipping the substrate in hydrofluoricacid (HF). In another embodiment, the partially removing the isolationinsulating layer 50 may be performed using a dry etching process. Forexample, a dry etching process using CHF₃ or BF₃ as etching gases may beused.

As shown in FIG. 1C, and as described in example operation 110 of FIG.3, a germanium nitride layer 40 is formed on the semiconductor structure10. In the embodiments, germanium nitride layer 40 abuts thesemiconductor structure 10.

In embodiments, germanium nitride layer 40 is formed on at least onesurface of the semiconductor structure 10. As shown in FIG. 1C, inembodiments, germanium nitride layer 40 is formed on exposed surfaces ofsemiconductor structure 10.

In embodiments, the germanium nitride layer 40 is more than a monolayerthick. Accordingly, embodiments of the present disclosure include adevice comprising a germanium nitride layer 40 that is more than amonolayer thick on a surface of a semiconductor structure 10 thatcomprises germanium. Additional embodiments of the present disclosureinclude methods comprising forming a semiconductor structure 10comprising germanium, and forming a germanium nitride layer 40 having athickness that is more than a monolayer on the semiconductor structure10.

Such embodiments provide better reliability through improvedreproducibility and durability under thermal load as compared to atraditional surface passivation layer (e.g., a monolayer ofgermaniumoxynitride (GeON)).

Without proper surface passivation, germanium-containing nanowires andfins may suffer from high interfacial states. In embodiments, the D_(IT)of an interface between the surface of the semiconductor structure 10and germanium nitride layer 40 is no more than about 5×10¹¹ eV⁻¹ cm⁻² Inembodiments, the D_(IT) of an interface between the surface of thesemiconductor structure 10 and germanium nitride layer 40 is less thanabout 5×10¹¹ eV⁻¹ cm². In embodiments, the D_(IT) of an interfacebetween the surface of the semiconductor structure 10 and germaniumnitride layer 40 ranges from about 1×10¹¹ eV⁻¹ cm⁻² to about 5×10¹¹ eV⁻¹cm⁻².

In embodiments, the germanium nitride layer 40 is at least a bilayerthick. In embodiments, the germanium nitride layer 40 is more than abilayer thick. In embodiments, the germanium nitride layer 40 is atleast a trilayer thick. In embodiments, the germanium nitride layer 40is more than a trilayer thick.

In some embodiments, a germanium nitride layer 40 is at least about 0.2nanometers (nm) thick. In some embodiments, a germanium nitride layer 40is at least about 0.5 nm thick. In some embodiments, a germanium nitridelayer 40 is at least about 1.0 nm thick. In some embodiments, agermanium nitride layer 40 is at least about 1.5 nm thick. In someembodiments, a germanium nitride layer 40 is no more than about 2.5 nmthick. In some embodiments, a germanium nitride layer 40 is no more thanabout 2.0 nm thick. In some embodiments, a germanium nitride layer 40 isno more than about 1.5 nm thick. In some embodiments, the thickness of agermanium nitride layer 40 ranges from about 0.2 nm to about 2.0 nm.

In some embodiments, a germanium nitride layer 40 has a substantiallyuniform thickness. “Substantially uniform thickness,” as used hereinmeans that the layer has an overall thickness variation of less than±30% from the average thickness of the layer. In embodiments,substantially uniform thickness means that the layer has an overallthickness variation of less than ±25% from the average thickness. Insome embodiments, substantially uniform thickness means that the layerhas an overall thickness variation of less than ±20% from the averagethickness. In some embodiments, substantially uniform thickness meansthat the layer has an overall thickness variation of less than ±15% fromthe average thickness. In some embodiments, substantially uniformthickness means that the layer has an overall thickness variation ofless than ±10% from the average thickness. In some embodiments,substantially uniform thickness means that the layer has an overallthickness variation of less than ±5% from the average thickness.

In embodiments, a germanium nitride layer 40 is formed using chemicalvapor deposition (CVD). In some embodiments, a germanium nitride layer40 is formed using metal-organic chemical vapor deposition (MOCVD). Insuch embodiments, semiconductor structure 10 is exposed to a vapor thatincludes germanium. In embodiments, the vapor includes one or morevolatile precursors that decompose and/or react to deposit germaniumnitride on the surface of semiconductor structure 10. In someembodiments, the vapor comprises Ge₂H₆. In some embodiments, the vaporcomprises GeH₄.

In some embodiments, the vapor further comprises N₂H₄. In embodiments,the N₂H₄ source is anhydrous. In such embodiments, the oxygenconcentration of germanium nitride layer 40 is about zero. In otherwords, in accordance with embodiments of the present disclosure,germanium nitride layer 40 has substantially zero oxygen impurities. Inembodiments, a germanium nitride layer 40 formed using N₂H₄ has fewernitrogen vacancies than a germanium nitride layer 40 formed using NH₃.In some such embodiments, the nitrogen vacancies are less than about5×10¹⁶ atoms/cm⁻³. In some embodiments, the nitrogen vacancies are lessthan about 4×10¹⁶ atoms/cm⁻³. In certain embodiments, the vaporcomprises Ge₂H₆ and N₂H₄.

In embodiments, the vapor does not comprise a precursor that containscarbon. In such embodiments, the carbon concentration of the germaniumnitride layer 40 is lower than the carbon concentration of a comparablegermanium nitride layer formed using a carbon containing precursor. Insome embodiments, the carbon concentration of the germanium nitridelayer 40 is no more than about 5×10¹⁶ atoms/cm⁻³. In some embodiments,the carbon concentration of the germanium nitride layer 40 is less than5×10¹⁶ atoms/cm⁻³.

In some embodiments, the germanium nitride layer 40 consists essentiallyof germanium nitride. In such embodiments, the germanium nitride layer40 has a carbon concentration of no more than about 5×10¹⁶ atoms/cm⁻³,and an oxygen concentration of substantially zero.

The germanium nitride layer 40 may be formed using any suitableprocessing parameters (e.g., flow rate, wafer temperature, pressure,deposition time, etc.). In embodiments, a component of the vapor (e.g.,Ge₂H₆, N₂H₄, etc.) has a flow rate ranging from about 10 standard cubiccentimeters per minute (sccm) to about 800 sccm. In embodiments, acomponent of the vapor has a flow rate ranging from about 20 sccm toabout 800 sccm. In some embodiments, the vapor has a flow rate rangingfrom about 10 sccm to about 800 sccm. In some embodiments, the vapor hasa flow rate ranging from about 20 sccm to about 800 sccm.

In accordance with methods of the present disclosure, a germaniumnitride layer 40 is formed on a germanium-containing semiconductorstructure 10 at temperatures that are sufficiently low to avoid reflowof the germanium of the semiconductor structure.

In some embodiments, a semiconductor structure 10 is exposed to thevapor with a wafer temperature that is no more than about 500° C. Insome embodiments, a semiconductor structure 10 is exposed to the vaporwith a wafer temperature that is less than about 500° C. In variousembodiments, semiconductor structure 10 is exposed to the vapor with awafer temperature that is no more than about 450° C. In variousembodiments, semiconductor structure 10 is exposed to the vapor with awafer temperature that is less than about 450° C. In variousembodiments, semiconductor structure 10 is exposed to the vapor with awafer temperature that is no more than about 400° C. In variousembodiments, semiconductor structure 10 is exposed to the vapor with awafer temperature that is at least about 330° C. In various embodiments,semiconductor structure 10 is exposed to the vapor with a wafertemperature that is at least about 340° C. In some embodiments,semiconductor structure 10 is exposed to the vapor with a wafertemperature ranging from about 340° C. to about 500° C. In someembodiments, semiconductor structure 10 is exposed to the vapor with awafer temperature ranging from about 340° C. to about 450° C. In someembodiments, semiconductor structure 10 is exposed to the vapor with awafer temperature ranging from about 440° C. to about 500° C. In someembodiments, semiconductor structure 10 is exposed to the vapor with awafer temperature ranging from about 340° C. to about 400° C.

In embodiments, semiconductor structure 10 is exposed to the vapor at apressure that is no more than about 300 Torr. In embodiments,semiconductor structure 10 is exposed to the vapor at a pressure that isless than about 300 Torr. In embodiments, semiconductor structure 10 isexposed to the vapor at a pressure that is no more than about 100 Torr.In embodiments, semiconductor structure 10 is exposed to the vapor at apressure that is less than about 100 Torr. In various embodiments,semiconductor structure 10 is exposed to the vapor at a pressure that isno more than about 50 Torr. In some embodiments, semiconductor structure10 is exposed to the vapor at a pressure that ranges from about 10 Torrto about 300 Torr. In some embodiments, semiconductor structure 10 isexposed to the vapor at a pressure that ranges from about 10 Torr toabout 100 Torr. In certain embodiments, semiconductor structure 10 isexposed to the vapor at a pressure that ranges from about 10 Torr toabout 50 Torr.

In embodiments, the pressure at which semiconductor structure 10 isexposed to the vapor is modulated in order to control the efficiency ofthe growth of germanium nitride layer 40. In such embodiments, reducingthe pressure at which semiconductor structure 10 is exposed increasesthe efficiency of the growth of germanium nitride layer 40.

In embodiments, the deposition time for forming a germanium nitridelayer 40 of the present disclosure is significantly less than thedeposition time for growing a silicon cap layer at the same temperature.In embodiments, the deposition time for a germanium nitride layer 40 isless than 500 seconds. In embodiments, the deposition time for agermanium nitride layer 40 is less than 400 seconds. In embodiments, thedeposition time for a germanium nitride layer 40 is less than 250seconds. In embodiments, the deposition time for a germanium nitridelayer 40 is less than 200 seconds. In embodiments, the deposition timefor a germanium nitride layer 40 is less than 100 seconds.

In embodiments, the inhibition time for forming a germanium nitridelayer 40 of the present disclosure is significantly less than theinhibition time for growing a silicon cap layer at the same temperature.As used herein, “inhibition time” refers to the period of time betweenthe start of a CVD process (i.e., exposure of a semiconductor structureto a vapor) and the start of the epitaxial growth on the surface of thesemiconductor structure. A lower inhibition time may result in a moreuniform thickness in the layer. In embodiments, the inhibition time forgrowing a silicon cap layer ranges from about 10 seconds to about 30seconds. In some embodiments, there is substantially no inhibition timefor forming a germanium nitride layer 40.

As shown in FIG. 1D, in accordance with embodiments of the presentdisclosure, a gate dielectric layer 60 is formed on the germaniumnitride layer 40. In other words, the germanium nitride layer 40 isbetween the gate dielectric layer 60 and the semiconductor structure 10.In embodiments, gate dielectric layer 60 abuts germanium nitride layer40. Gate dielectric layer 60 may be formed using any suitable method,such as atomic layer deposition (ALD) and the like.

In some embodiments, gate dielectric layer 60 is a high-k dielectric. Insome embodiments, the high-k dielectric has a k value greater than about7.0, and may include a metal oxide, nitride, or a silicate of hafnium,aluminum, zirconium, lanthanum (La), and the like. In some embodiments,the high-k dielectric comprises an oxide or nitride of hafnium,aluminum, lanthanum, lutetium (Lu), zirconium, titanium, tantalum,barium (Ba), strontium (Sr), lead (Pb), and the like. In certainembodiments, the high-k dielectric comprises hafnium oxide, zirconiumoxide, or the like.

In embodiments, the gate dielectric layer 60 also includes aninterfacial layer. In some embodiments, the interfacial layer is made ofsilicon dioxide.

As shown in FIG. 1E, in accordance with embodiments of the presentdisclosure, a gate electrode 65 is formed on the gate dielectric layer60. Any suitable method may be used to form a gate electrode 65. Invarious embodiments, a gate electrode 65 is formed using a conformalmethod. Gate electrode 65 may include Ti, Ta, tungsten (W), molybdenum(Mo), Ru, Pt, Co, Ni, Pd, niobium (Nb), Al, copper (Cu), or alloysthereof. In embodiments, gate electrode 65 includes a metal-containingmaterial, such as titanium nitride (TiN), tantalum carbide (TaC),tantalum nitride (TaN), tantalum aluminum carbide (TaAlC), titaniumcarbide (TiC), Co, Al, titanium aluminide (TiAl), Hifi, titaniumsilicide (TiSi), tantalum silicide (TaSi), or titanium aluminum carbide(TiAlC).

In some embodiments, gate electrode 65 includes more than one layer of ametal, a metal alloy, a metal-containing material, or a combinationthereof. In various embodiments, gate electrode 65 includes a workfunction metal layer. In some embodiments, work function metal layerincludes one or more layers of metal materials, such as TiN, TaN, TaAlC,TiC, TaC, Co, Al, TiAl, HfTi, TiSi, TaSi, or TiAlC.

In embodiments, a channel region 70 is formed in a portion ofsemiconductor structure 10. In various embodiments, the germaniumnitride layer 40 is on the channel region 70 of the transistor. Inembodiments, such as the embodiment shown in 1E, the portion ofsemiconductor structure 10 on which germanium nitride layer 40 is formedis the channel region 70.

Accordingly, embodiments of the present disclosure include a devicecomprising a substrate 20, a semiconductor structure 10 comprisinggermanium, a channel region 70 in the semiconductor structure 10, and agermanium nitride layer 40 on the channel region 70, the germaniumnitride layer 40 having a thickness that is more than a monolayer.Additional embodiments of the present disclosure include methodscomprising forming a germanium nitride layer 40 having a thickness thatis more than a monolayer on a channel region 70 in a semiconductorstructure 10 that comprises germanium.

FIGS. 2A-2G illustrate steps of a method of the disclosure, inaccordance with some embodiments of the present disclosure. FIGS. 2A-2Eillustrate steps of a method of forming the structure of FIG. 2E as across sectional view along the line A-A indicated in FIG. 2A, inaccordance with some embodiments of the present disclosure. FIGS. 2F and2G are illustrations of two embodiments of the present disclosure thatinclude multiple semiconductor structures.

Semiconductor structure 10 (e.g., a nanowire or a fin) includinggermanium is formed, as shown in FIG. 2A, and as described above withregard to FIG. 1A. As shown in FIG. 2A, semiconductor structure 10 is ananowire, in some embodiments.

In embodiments, a semiconductor structure 10 is formed on a substrate20. In some embodiments, a semiconductor substrate 10 is spaced apartfrom a surface 25 of the substrate 20, as shown in FIG. 2A.

In some embodiments, a semiconductor structure 10 is a horizontalsemiconductor structure, i.e., a semiconductor structure that has aheight 30 that is substantially equal to or less than the width 35 ofthe semiconductor structure 10, as shown in FIG. 2B, which shows across-sectional view along line A-A of FIG. 2A. “Substantially,” as usedherein means that the height 30 of a semiconductor structure 10 iswithin ±30% of the width 35 of the semiconductor structure 10. Inembodiments, substantially means that the height 30 of a semiconductorstructure 10 is within ±25% of the width 35 of the semiconductorstructure 10. In embodiments, substantially means that the height 30 ofa semiconductor structure 10 is within ±20% of the width 35 of thesemiconductor structure 10. In embodiments, substantially means that theheight 30 of a semiconductor structure 10 is within ±15% of the width 35of the semiconductor structure 10. In embodiments, substantially meansthat the height 30 of a semiconductor structure 10 is within ±10% of thewidth 35 of the semiconductor structure 10. In embodiments,substantially means that the height 30 of a semiconductor structure 10is within ±5% of the width 35 of the semiconductor structure 10.

In some such embodiments, a horizontal semiconductor structure is ahorizontal nanowire or horizontal semiconductor strip. In otherembodiments, a horizontal semiconductor structure is a fin.

In various embodiments, more than one semiconductor structure 10 ispresent. For example, multiple horizontal nanowires may be included in astacked configuration, as shown in FIGS. 2F and 2G. In some embodiments,a second horizontal nanowire is formed over, and aligned with, a firsthorizontal nanowire on a substrate. In certain embodiments, a thirdhorizontal nanowire is formed over, and aligned with, the secondhorizontal nanowire. In other embodiments, the multiple horizontalnanowires are not arranged in a stacked configuration. For example, thesecond horizontal nanowire is formed laterally adjacent to and alignedwith, a first nanowire on a substrate. In certain embodiments, a thirdhorizontal nanowire is formed laterally adjacent to and aligned with,the second horizontal nanowire.

Germanium nitride layer 40 is then formed on semiconductor structure 10using methods of the present disclosure, as shown in FIG. 2C and asdescribed above with regard to FIG. 1C. Such methods may havesignificantly less than the inhibition time than methods for growing asilicon cap layer at the same temperature, and produce a germaniumnitride layer 40 that is more than a monolayer thick, and may have asubstantially uniform thickness. Methods of the present disclosure canbe used to form a germanium nitride layer 40 with low levels ofcontamination, including low levels of carbon contamination, oxygencontamination, or both, as well as low levels of nitrogen vacancies.Such a germanium nitride layer 40 may be more reliable due to anincrease in reproducibility and durability under thermal load ascompared to a traditional surface passivation layer.

As shown in FIG. 2C, in embodiments, the germanium nitride layer 40 isformed on the exposed surface of the semiconductor structure 10. In someembodiments, germanium nitride layer 40 surrounds the semiconductorstructure 10. In some embodiments, the germanium nitride layer 40 isarranged between the semiconductor structure 10 and the substrate 20.

In some embodiments where more than one semiconductor structure 10 ispresent, a germanium nitride layer 40 is formed on at least one of thesemiconductor structures 10. In some such embodiments, a germaniumnitride layer is formed on a subset of the semiconductor structures. Inother embodiments, a germanium nitride layer is formed on each of thesemiconductor structures, as shown in FIGS. 2F and 2G. In variousembodiments, a germanium nitride layer is between a first semiconductorstructure and a second semiconductor structure.

In embodiments, semiconductor structure 10 includes a channel region 70.In various embodiments, the germanium nitride layer 40 is on the channelregion 70. In embodiments, such as the embodiment shown in FIG. 2E, theportion of semiconductor structure 10 around which germanium nitridelayer 40 is formed is the channel region 70.

In some embodiments, the germanium nitride layer 40 surrounds channelregion 70. In other words, germanium nitride layer 40 wraps aroundchannel region 70 in semiconductor structure 10. In some embodiments,the germanium nitride layer 40 is arranged between the channel region 70and the substrate 20.

The gate structure can then be formed in accordance with embodiments ofthe disclosure. In embodiments, gate dielectric layer 60 is formed ongermanium nitride layer 40, as shown in FIG. 2D, and as described abovewith regard to FIG. 1D. In some embodiments, a gate dielectric layer 60surrounds germanium nitride layer 40. In some embodiments, the gatedielectric layer 60 is arranged between the semiconductor structure 10and the substrate 20. In some embodiments, the gate dielectric layer 60is arranged between the channel region 70 and the substrate 20.

In embodiments, a gate electrode 65 is formed on gate dielectric layer60, as shown in FIG. 2E, and as described above with regard to FIG. 1E.In various embodiments, gate electrode 65 surrounds the gate dielectriclayer 60. In some embodiments, the gate electrode 65 is arranged betweenthe semiconductor structure 10 and the substrate 20. In someembodiments, the gate electrode 65 is arranged between the channelregion 70 and the substrate 20.

In some embodiments, the germanium nitride layer 40 and semiconductorstructure 10 are part of a vertical or horizontal gate all around (GAA)structure, as shown in FIGS. 2E and 2F. The GAA transistor structuresmay be patterned by any suitable method. For example, the structures maybe patterned using one or more photolithography processes, includingdouble-patterning or multi-patterning processes. Generally,double-patterning or multi-patterning processes combine photolithographyand self-aligned processes, allowing patterns to be created that have,for example, pitches smaller than what is otherwise obtainable using asingle, direct photolithography process. For example, in one embodiment,a sacrificial layer is formed over a substrate and patterned using aphotolithography process. Spacers are formed alongside the patternedsacrificial layer using a self-aligned process. The sacrificial layer isthen removed, and the remaining spacers may then be used to pattern theGAA structure.

In embodiments, a device in accordance with the present disclosurecomprises a germanium nitride layer on a semiconductor structure asdescribed herein. In embodiments, the germanium nitride layer andsemiconductor structure are part of a vertical tunneling field effecttransistor (TFET), a finFET, a horizontal nanowire FET, a verticalnanowire FET or the like.

In various embodiments, a device of the present disclosure is a finFET.In other embodiments, a device of the present disclosure is a nanowireFET. In some embodiments, a device of the present disclosure is ahorizontal nanowire FET. In some embodiments, a device of the presentdisclosure is a vertical nanowire FET. An embodiment of a nanowire FETaccording to some embodiments of the disclosure is illustrated in FIGS.2E-2G.

The present disclosure provides, in various embodiments, a device thatincludes a semiconductor structure that is on a substrate and includesgermanium, where a layer of germanium nitride that is more than amonolayer thick is on the semiconductor structure.

Embodiments of the present disclosure further include a device thatincludes a germanium nitride layer that is more than a monolayer thickon a channel region in a semiconductor structure arranged on asubstrate.

The present disclosure also provides, in various embodiments, a devicethat includes a germanium nanowire on a substrate, where a germaniumnitride layer that is more than a monolayer thick surrounds a channelformed in the germanium nanowire.

Embodiments of the present disclosure also include a device thatincludes a germanium fin structure formed on a substrate, where agermanium nitride layer that is more than a monolayer thick is formedover a channel formed in the germanium fin structure.

Embodiments of the present disclosure further include a method offorming a layer of germanium nitride that is more than a monolayer thickon a semiconductor structure that includes germanium.

The foregoing outlines features of several embodiments so that thoseskilled in the art may better understand the aspects of the presentdisclosure. Those skilled in the art should appreciate that they mayreadily use the present disclosure as a basis for designing or modifyingother processes and structures for carrying out the same purposes and/orachieving the same advantages of the embodiments introduced herein.Those skilled in the art should also realize that such equivalentconstructions do not depart from the spirit and scope of the presentdisclosure, and that they may make various changes, substitutions, andalterations herein without departing from the spirit and scope of thepresent disclosure.

The various embodiments described above can be combined to providefurther embodiments. These and other changes can be made to theembodiments in light of the above-detailed description. In general, inthe following claims, the terms used should not be construed to limitthe claims to the specific embodiments disclosed in the specificationand the claims, but should be construed to include all possibleembodiments along with the full scope of equivalents to which suchclaims are entitled. Accordingly, the claims are not limited by thedisclosure.

1. A device comprising: a semiconductor substrate; a germanium nanowireon the semiconductor substrate, the germanium nanowire comprising achannel; and a germanium nitride layer surrounding a circumference ofthe channel, the germanium nitride layer having a thickness that is morethan a monolayer.
 2. The device of claim 1, wherein the germaniumnitride layer has a carbon concentration of no more than about 5×10¹⁶atoms/cm⁻³.
 3. The device of claim 1, wherein an interface between thegermanium nanowire and the germanium nitride layer has an interface trapdensity (D_(IT)) of no more than about 5×10¹¹ eV⁻¹ cm⁻².
 4. The deviceof claim 1, wherein a surface of the semiconductor substrate underlyingthe channel is spaced apart from a bottom surface of the channel.
 5. Thedevice of claim 1, wherein the germanium nitride layer is between thegermanium nanowire and the semiconductor substrate.
 6. The device ofclaim 1, wherein the semiconductor substrate abuts the germanium nitridelayer.
 7. The device of claim 1, further comprising a dielectric layeron the germanium nitride layer, the dielectric layer surrounding thecircumference of the channel.
 8. The device of claim 7, furthercomprising a gate electrode on the dielectric layer, the gate electrodesurrounding the circumference of the channel.
 9. A device comprising: asubstrate; a fin structure on the substrate, the fin structurecomprising germanium; a channel region in the fin structure; and agermanium nitride layer on the channel region, the germanium nitridelayer having a thickness that is more than a monolayer.
 10. The deviceof claim 9 further comprising a gate dielectric layer on the germaniumnitride layer, such that the germanium nitride layer is between the gatedielectric layer and the fin structure.
 11. The device of claim 10further comprising isolation regions along opposing sides of the finstructure, wherein the germanium nitride layer extends over theisolation regions.
 12. The device of claim 11, wherein the germaniumnitride layer completely separates the gate dielectric layer from theisolation regions.
 13. The device of claim 9, wherein the substrate hasa surface, the fin structure having a width and a height that is greaterthan the width, the fin structure extending away from the surface of thesubstrate to the height.
 14. The device of claim 9, wherein thethickness of the germanium nitride layer is at least about 1 nanometer.15. A device comprising: a first nanostructure and a secondnanostructure over a substrate, the first nanostructure and the secondnanostructure comprising a germanium-containing material; a firstgermanium nitride layer over the first nanostructure and a secondgermanium nitride layer over the second nanostructure, the firstgermanium nitride layer and the second germanium nitride layer having athickness that is more than a monolayer; a first dielectric layer overthe first germanium nitride layer and a second dielectric layer over thesecond germanium nitride layer; a source region and a drain region, thefirst nanostructure and the second nanostructure being interposedbetween the source region and the drain region; and a gate electrodeover the first dielectric layer and the second dielectric layer.
 16. Thedevice of claim 15, wherein the first germanium nitride layer isseparated from the second germanium nitride layer.
 17. The device ofclaim 15, wherein a carbon concentration of the first germanium nitridelayer is no more than about 5×10¹⁶ atoms/cm⁻³.
 18. The device of claim15, wherein an interface trap density (DIT) of an interface between thefirst nanostructure and the first germanium nitride layer is less thanabout 5×1011 eV⁻¹ cm⁻².
 19. The device of claim 15, wherein the firstgermanium nitride layer is free of oxygen.
 20. The device of claim 15,wherein a region between the first nanostructure and the substrate isfree of other germanium-containing nanostructures, and wherein the gateelectrode extends between the first nanostructure and the substrate.